As a non-shrink filler and repair compound, which can be overcoated with either an epoxy or polyester/vinyl ester top coat. It may also be used as a standalone grouting or filling compound.

Consult the Health & Safety data sheet prior to carrying out any work with this product.

For the best result, the surface should be blast cleaned to SSPC-SP10 (ISO8501-1 Sa 2½) with a 3 mil (75micron)profile. If grit blasting is not possible the surface should be degreased, loose material removed and the surface roughened to obtain a suitable key.

Short hair stiff brush, trowel, float or mastic type gun.

Remove the lids from both the base and activator. Add between 1% and 2% of adhesion promoter to the base and mix in thoroughly. Add all of the activator to the base and mix thoroughly, ensuring no unmixed material remains. Remove all the mixed material from the base tin and re-mix on a clean flat surface or in a clean shallow receptacle.This product has a relatively short pot life, mix only as much material as you can apply within this period.

This material is intended for use as a filler or grouting materialand can be built up to the required film thickness. It should, where possible, be applied over a primer layer or correctly prepared substrate. Application of films greater than 6mm in one coat should be avoided, to prevent excessive exotherms during cure. Incorporation of the adhesion promoter will substantially improve the bond in all cases, both intercoat and to the substrate.

100%.

Approximately 36-38 sf per gal (0.90 – 0.95m²/litre) @ 1mm DFT.

NOTE: This information is given in good faith but may increase dependent upon environment conditions, the geometry and nature of work undertaken and the skill and care in application. Corrocoat accepts no responsibility for any deviation from these values.

There is no minimum overcoating window. The next coat can be applied as soon as previous coat has gelled enough to support its own weight.
Maximum overcoating window: Up to 96 hours at 68°F (20°C) are acceptable.

Greater than 212°F (100°C).

Modified Amine.